Heat Resistant Aluminum Paint
Types
1.Aluminum paints 600 C Heat Stability
2.Aluminum paints 250 C Heat Stability
1 . 600C Heat Stability Aluminum Paint
600 C Heat stability aluminum paints are made from silicon resin, aluminum finish is more effective in commercial and light industrial application like chimney, boiler etc… where corrosion and heat resistance are more important than chemical and abrasion resistance. Because of the nature of aluminum particles aluminum finish offers superior moisture and heat resistance then similar coating pigment with titanium dioxide & other pigments.
Technical Information
| Finish | Semi-Gloss |
| Colour | Silver |
| Clean-up Thinner | Xylene |
| Sp. Gravity | 0.9-1.00 |
| Practical Converge | 150-175 sq.ft/liter |
| % Age Solid | 42-45 |
| Viscosity | 60-70 Seconds in Ford Cup B4 at 30 C Temp |
| Thinner | Xylene |
Recommended Primer
- Self Priming or high temp black primer
Surface Preparation
- II surfaces must be dry, clean, free from oil, grease and any foreign particles
Feature
- High durable and weather resistance
- Corrosion and Heat Resistance up to 600 C temp
Drying Time
- Surface Dry – 30 Min
- Tack Free –1 to 2 hours
- Hard Dry – After getting temperature above 100 C.
Packaging
- Available in 1 liter and 4 liter containers
2. 250 C Heat Stability Aluminum Paint
Description
Aluminum Paints are made form modified petroleum resins, aluminum finishes are effective in commercial and light industrial application where corrosion and/or temperature resistance are more important than chemical and abrasion resistance. Because of the nature of aluminum particles aluminum offers superior moisture and heat resistance then similar coating pigment with titanium dioxide and other pigments.
Technical Information
| Finish | Semi-Gloss |
| Colour | Silver |
| Clean-up Thinner | Mineral Spirit |
| Sp. Gravity | 0.9 – 1.0 |
| Practical Coverage | 150-175 Sq.ft/Liter |
| % Age Solid | 40-43 |
| Viscosity | 40-50 Sec. in Ford Cup B4 at 30C |
| Thinner | Mineral Spirit |
Recommended Primer
- Self Priming on Metal
Surface Preparation
- II Surface must be dry, clean, free from oil, grease and any foreign particles.
Feature
- High durable and weather resistance
- Corrosion and Heat Resistance up to 200 C temp
Drying Time
- Surface Dry – 45 Min
- Tack Free –1 to 2 hours
- Hard Dry – After getting temperature above 100 C.